Sample testing confirms that these are equal to their originals. Nylon, PLA and PVA were already optimised, but ABS and CPE weren't. Now all are optimised except some 0.4mm core profiles. I'll see to those next. Note that the filament flow compensation setting is still wrong in these profiles (it was wrong in the original profiles as well). Contributes to issue CURA-3650.
36 lines
1.2 KiB
INI
36 lines
1.2 KiB
INI
[general]
|
|
version = 2
|
|
name = Draft Print
|
|
definition = ultimaker3
|
|
|
|
[metadata]
|
|
type = quality
|
|
quality_type = draft
|
|
material = generic_pla_ultimaker3_AA_0.8
|
|
weight = -2
|
|
|
|
[values]
|
|
cool_fan_full_at_height = =layer_height_0 + 2 * layer_height
|
|
cool_fan_speed_max = =cool_fan_speed
|
|
cool_min_speed = 2
|
|
gradual_infill_step_height = =3 * layer_height
|
|
gradual_infill_steps = 4
|
|
infill_line_width = =round(line_width * 0.535 / 0.75, 2)
|
|
infill_pattern = cubic
|
|
infill_sparse_density = 80
|
|
line_width = =machine_nozzle_size * 0.9375
|
|
machine_nozzle_cool_down_speed = 0.75
|
|
machine_nozzle_heat_up_speed = 1.6
|
|
material_final_print_temperature = =max(-273.15, material_print_temperature - 15)
|
|
material_initial_print_temperature = =max(-273.15, material_print_temperature - 10)
|
|
material_print_temperature = =default_material_print_temperature + 10
|
|
material_standby_temperature = 100
|
|
prime_tower_size = 15
|
|
support_angle = 70
|
|
support_line_width = =line_width * 0.75
|
|
support_xy_distance = =wall_line_width_0 * 1.5
|
|
top_bottom_thickness = =layer_height * 4
|
|
wall_line_width = =round(line_width * 0.75 / 0.75, 2)
|
|
wall_line_width_x = =round(wall_line_width * 0.625 / 0.75, 2)
|
|
wall_thickness = =wall_line_width_0 + wall_line_width_x
|
|
|